Machined Plastics
| HPU/92 Shore A | ||||||
|---|---|---|---|---|---|---|
| Thermoplastic polyurethane with resistance to hydrolysis | ||||||
| Properties | condition | standard | unit | |||
| color | red | red | ||||
| hardness | 23° C | ISO 868 | shore A | 95÷2 | shore A | 95÷2 |
| hardness | 23° C | ISO 868 | shore D | 48÷3 | shore D | 48÷3 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 15 | psi | 2175 |
| modulus 300% | 23° C | DIN 53 504 | MPa | 28 | psi | 4160 |
| tensile strength | 23° C | DIN 53 504 | Mpa | 50 | psi | 7250 |
| elongation at break | 23° C | DIN 53 504 | % | 350 | % | 350 |
| tear strength | 23° C | DIN ISO 34-1 Methode B | kN/m | 110 | lbf/inch | 570 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1200 | g/cm3 | 1,2 |
| abrasion | 23° C | DIN 53 516 | mm3 | 17 | mm3 | 17 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 27 | % | 27 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 33 | % | 33 |
| minimum service temp. | °C | -20 | °F | -4 | ||
| maximum service temp. | °C | 115 | °F | 240 | ||
| C-HPU Hardness 96 Shore A red | ||||||
|---|---|---|---|---|---|---|
| Casted thermoplastic polyurethane with resistance to hyrolysis (TPU) | ||||||
| Properties | condition | standard | unit | |||
| color | red | red | ||||
| hardness | 23° C | ISO 868 | shore A | 96÷2 | shore A | 96÷2 |
| hardness | 23° C | ISO 868 | shore D | 50÷3 | shore D | 50÷3 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 12 | psi | 1740 |
| modulus 300% | 23° C | DIN 53 504 | MPa | 22 | psi | 3190 |
| tensile strength | 23° C | DIN 53 504 | Mpa | 45 | psi | 6525 |
| elongation at break | 23° C | DIN 53 504 | % | 450 | % | 450 |
| tear strength | 23° C | DIN ISO 34-1 Methode B | kN/m | 80 | lbf/inch | 450 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1130 | g/cm3 | 1,13 |
| abrasion | 23° C | DIN 53 516 | mm3 | 20 | mm3 | 20 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 30 | % | 30 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 35 | % | 35 |
| minimum service temp. | °C | -37 | °F | -35 | ||
| maximum service temp. | °C | 110 | °F | 230 | ||
| maximum water steam temp. | °C | 90 | °F | 195 | ||
| LT-PU Hardness 96 Shore A blue | ||||||
|---|---|---|---|---|---|---|
| Thermoplastic polyurethane for low-temperature applications | ||||||
| Properties | condition | standard | unit | |||
| color | blue | blue | ||||
| hardness | 23° C | ISO 868 | shore A | 96÷2 | shore A | 96÷2 |
| hardness | 23° C | ISO 868 | shore D | 47÷3 | shore D | 47÷3 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 12 | psi | 1740 |
| modulus 300% | 23° C | DIN 53 504 | MPa | 22 | psi | 3190 |
| tensile strength | 23° C | DIN 53 504 | MPa | 50 | psi | 7250 |
| elongation at break | 23° C | DIN 53 504 | % | 550 | % | 550 |
| tear strength | 23° C | DIN ISO 34-1 Methode B | kN/m | 80 | lbf/inch | 450 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1170 | g/cm3 | 1,17 |
| abrasion | 23° C | DIN 53 516 | mm3 | 17 | mm3 | 17 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 27 | % | 27 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 33 | % | 33 |
| minimum service temp. | °C | -50 | °F | -58 | ||
| maximum service temp. | °C | 110 | °F | 230 | ||
| HT-PU Hardness 96 Shore A | ||||||
|---|---|---|---|---|---|---|
| Thermoplastic polyurethane for high-temperature applications | ||||||
| properties | condition | standard | unit | |||
| color | ||||||
| hardness | 23° C | ISO 868 | shore A | 96÷2 | shore A | 96÷2 |
| hardness | 23° C | ISO 868 | shore D | 50÷3 | shore D | 50÷3 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 11 | psi | 1595 |
| modulus 300% | 23° C | DIN 53 504 | MPa | 22 | psi | 3190 |
| tensile strength | 23° C | DIN 53 504 | MPa | 45 | psi | 6525 |
| elongation at break | 23° C | DIN 53 504 | % | 500 | % | 500 |
| tear strength | 23° C | DIN ISO 34-1 Methode B | kN/m | 80 | lbf/inch | 450 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1170 | g/cm3 | 1,17 |
| abrasion | 23° C | DIN 53 516 | mm3 | 15 | mm3 | 15 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 32 | % | 32 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 35 | % | 35 |
| compression set | 24h 125° C 25% deflection | ISO 815 | % | 50 | % | 50 |
| minimum service temp. | °C | -35 | °F | -31 | ||
| maximum service temp. | °C | 135 | °F | 275 | ||
| maximum service temp. (short) | °C | 150 | °F | 300 | ||
| NBR Hardness 85 Shore A Black | ||||||
|---|---|---|---|---|---|---|
| Nitrile butadiene rubber | ||||||
| properties | condition | standard | unit | |||
| color | black | black | ||||
| hardness | 23° C | ISO 868 | shore A | 85÷5 | shore A | 85÷5 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 11 | psi | 1595 |
| tensile strength | 23° C | DIN 53 504 | MPa | 17 | psi | 2465 |
| elongation at break | 23° C | DIN 53 504 | % | 150 | % | 150 |
| tear strength | 23° C | DIN ISO 34-1 | kN/m | 18 | lbf/inch | 102 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1320 | g/cm3 | 1,32 |
| rebound elasticity | 23° C | DIN 53 512 | % | 20 | % | 20 |
| abrasion | 23° C | DIN 53 516 | mm3 | 100 | mm3 | 100 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 5 | % | 5 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 6 | % | 6 |
| compression set | 24h 150° C 25% deflection | ISO 815 | % | % | ||
| minimum service temp. | °C | -30 | °F | -22 | ||
| maximum service temp. | °C | 110 | °F | 230 | ||
| H-NBR Hardness 85 Shore A Green | ||||||
|---|---|---|---|---|---|---|
| Highly saturated nitrile butadiene rubber | ||||||
| properties | condition | standard | unit | |||
| color | green | green | ||||
| hardness | 23° C | ISO 868 | shore A | 85÷5 | shore A | 85÷5 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 10 | psi | 1450 |
| tensile strength | 23° C | DIN 53 504 | MPa | 20 | psi | 2900 |
| elongation at break | 23° C | DIN 53 504 | % | 190 | % | 190 |
| tear strength | 23° C | DIN ISO 34-1 | kN/m | 15 | lbf/inch | 85 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1320 | g/cm3 | 1,32 |
| rebound elasticity | 23° C | DIN 53 512 | % | 30 | % | 30 |
| abrasion | 23° C | DIN 53 516 | mm3 | 135 | mm3 | 135 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 12 | % | 12 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 14 | % | 14 |
| compression set | 24h 150° C 25% deflection | ISO 815 | % | 22 | % | 22 |
| minimum service temp. | °C | -20 | °F | -4 | ||
| maximum service temp. | °C | 150 | °F | 302 | ||
| temp maximum water steam | °C | 120 | °F | 248 | ||
| temp maximum hot air | °C | 180 short | °F | 356 short | ||
| EPDM Peroxyd Hardness 85 Shore A Black | ||||||
|---|---|---|---|---|---|---|
| Ethylene Propylene diene rubber | ||||||
| properties | condition | standard | unit | |||
| color | green | green | ||||
| hardness | 23° C | ISO 868 | shore A | 85÷5 | shore A | 85÷5 |
| modulus 100% | 23° C | DIN 53 504 | MPa | psi | ||
| tensile strength | 23° C | DIN 53 504 | MPa | 12 | psi | 1740 |
| elongation at break | 23° C | DIN 53 504 | % | 80 | % | 80 |
| tear strength | 23° C | DIN ISO 34-1 | kN/m | 10 | lbf/inch | 55 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1220 | g/cm3 | 1,22 |
| rebound elasticity | 23° C | DIN 53 512 | % | 37 | % | 37 |
| abrasion | 23° C | DIN 53 516 | mm3 | 140 | mm3 | 140 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 7 | % | 7 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 7 | % | 7 |
| compression set | 24h 150° C 25% deflection | ISO 815 | % | % | ||
| minimum service temp. | °C | -45 | °F | -49 | ||
| maximum service temp. | °C | 130 | °F | 266 | ||
| temp maximum water steam | °C | 130 | °F | 266 | ||
| temp maximum hot air | °C | 180 short | °F | 356 short | ||
| MVQ Silicon Hardness 85 Shore A Blue | ||||||
|---|---|---|---|---|---|---|
| Vinyl methyl silicone rubber | ||||||
| properties | condition | standard | unit | |||
| color | blue | blue | ||||
| hardness | 23° C | ISO 868 | shore A | 85÷5 | shore A | 85÷5 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 4 | psi | 405 |
| tensile strength | 23° C | DIN 53 504 | MPa | 7 | psi | 710 |
| elongation at break | 23° C | DIN 53 504 | % | 120 | % | 120 |
| tear strength | 23° C | DIN ISO 34-1 Methode B |
kN/m | 15 | lbf/inch | 85 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 1580 | g/cm3 | 1,58 |
| rebound elasticity | 23° C | DIN 53 512 | % | 35 | % | 35 |
| abrasion | 23° C | DIN 53 516 | mm3 | mm3 | ||
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 8 | % | 8 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 9 | % | 9 |
| compression set | 24h 150° C 25% deflection | ISO 815 | % | % | ||
| minimum service temp. | °C | -60 | °F | -76 | ||
| maximum service temp. | °C | 200 | °F | 392 | ||
| temp maximum water steam | °C | °F | ||||
| temp maximum hot air | °C | 300 short | °F | 572 short | ||
| FPM Viton® Hardness 85 Shore A Brown | ||||||
|---|---|---|---|---|---|---|
| Fluorocarbon rubber | ||||||
| properties | condition | standard | unit | |||
| color | brown | brown | ||||
| hardness | 23° C | ISO 868 | shore A | 85÷5 | shore A | 85÷5 |
| modulus 100% | 23° C | DIN 53 504 | MPa | 6 | psi | 870 |
| tensile strength | 23° C | DIN 53 504 | MPa | 9 | psi | 1305 |
| elongation at break | 23° C | DIN 53 504 | % | 200 | % | 200 |
| tear strength | 23° C | DIN ISO 34-1 Methode B |
kN/m | 20 | lbf/inch | 114 |
| spec. gravity | 23° C | ISO 1183 | kg/m3 | 2530 | g/cm3 | 2,53 |
| rebound elasticity | 23° C | DIN 53 512 | % | 7 | % | 7 |
| abrasion | 23° C | DIN 53 516 | mm3 | 175 | mm3 | 175 |
| compression set | 24h 70° C 25% deflection | ISO 815 | % | 17 | % | 17 |
| compression set | 24h 100° C 25% deflection | ISO 815 | % | 10 | % | 10 |
| compression set | 24h 150° C 25% deflection | ISO 815 | % | 15 | % | 15 |
| minimum service temp. | °C | -20 | °F | -4 | ||
| maximum service temp. | °C | 220 | °F | 428 | ||
| temp maximum water steam | °C | °F | ||||
| temp maximum hot air | °C | 300 short | °F | 572 short | ||
| POM white | ||||||
|---|---|---|---|---|---|---|
| Polyoxymethelene/Polyacetal | ||||||
| properties | condition | standard | unit | |||
| color | white | white | ||||
| hardness | 23° C | ISO 868 | shore D | 85÷3 | shore D | 85÷3 |
| ball indentation hardness | 23° C | DIN 53456 H135/30 | MPa | 160 | psi | 23000 |
| tensile strength | 23° C | ASTM D 4745-79 | MPa | 70 | psi | 10100 |
| elongation at break | 23° C | ASTM D 4745-79 | % | 40 | % | 40 |
| compressive strength | 23° C | DIN 53456 | MPa | 88 | psi | 12800 |
| thermal conductivity | 23° C | DiN 52612 | J x 103 m x h x K |
0,25 | J x 103 m x h x K |
0,25 |
| coefficient of thermal expansion | 23° C C-200° C | K-1 x 10-5 | 11 | K-1 x 10-5 | 11 | |
| coefficient of friction* | 23° C | µ | 0,28 | µ | 0,28 | |
| minimum service temp. | °C | -45 | °F | -49 | ||
| maximum service temp. | °C | 100 | °F | 212 | ||
| Young's modulus | 23° C C | DIN 53457 | MPa | 3000 | psi | 435000 |
| * dynamic coefficient of friction, dry, Steel 16MnCR5: v=0,6m/s;p=0,05 MPa; t=5h | ||||||
| UHMW-PE Hardness 61 Shore D Natural | ||||||
|---|---|---|---|---|---|---|
| Polyethylene of ultra high molecular weight | ||||||
| properties | condition | standard | unit | |||
| color | natural | natural | ||||
| density/specific gravity | 23° C | DIN 53479 | kg/m3 | 930 | g/cm3 | 0,93 |
| hardness | 23° C | ISO 868 | shore D | 61÷3 | shore D | 61÷3 |
| ball indentation hardness | 23° C | DIN 53456 H135/30 | MPa | 36 | psi | 5200 |
| tensile strength | 23° C | ASTM D 4745-79 | MPa | 40 | psi | 5800 |
| elongation at break | 23° C | ASTM D 4745-79 | % | 50 | % | 50 |
| izod impact strength | 23° C | ISO 180/1A | kJ/m2 | 130 | ||
| thermal conductivity | 23° C | DiN 52612 | J x 103 m x h x K |
0,41 | J x 103 m x h x K |
0,41 |
| coefficient of thermal expansion | 25° -200° C | K-1 x 10-5 | 15 | K-1 x 10-5 | 15 | |
| coefficient of friction* | 23° C | µ | 0,25 | µ | 0,25 | |
| minimum service temp. | °C | -200 | °F | -328 | ||
| maximum service temp. | °C | 80 | °F | 176 | ||
| Young's modulus | 23° C C | DIN 53457 | MPa | 680 | psi | 98000 |
| * dynamic coefficient of friction, dry, Steel 16MnCR5: v=0,6m/s;p=0,05 MPa; t=5h | ||||||